RESUMO
The effects of low-cost Thai leucoxene mineral (LM) at different concentrations (10, 20, 30, 40, 50, and 60 mg/L) on the growth and antibacterial properties of Chrysanthemum indium L. cuttings under in vitro were evaluated. The primary chemical composition of LM was approximately 86% titanium dioxide (TiO2), as determined by dispersive X-ray spectroscopy. The crystalline structure, shape, and size were investigated by X-ray diffraction and scanning electron microscopy. LM at 40 and 50 mg/L significantly increased plant height, leaf number, node number, and fresh and dry weight. These growth-promoting properties were accompanied by improved chlorophyll and carotenoid contents and antioxidant enzyme activities and reduced malondialdehyde levels. Additionally, LM treatment at 40 and 50 mg/L had positive effects on antibacterial activity, as indicated by the lowest minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC) values. The high levels of phenolic compounds in the plants contributed to the MIC and MBC values. In conclusion, these findings provide evidence for the effectiveness of LM in enhancing the growth of Chrysanthemum plants in in vitro culture and improving their antibacterial abilities.
Assuntos
Antibacterianos , Chrysanthemum , Testes de Sensibilidade Microbiana , Antibacterianos/farmacologia , Antibacterianos/química , Antioxidantes/química , Carotenoides/química , Clorofila/química , Chrysanthemum/química , Folhas de Planta/química , Tailândia , Titânio/química , Titânio/farmacologiaRESUMO
High surface area nanosheet TiO2 with mesoporous structure were synthesized by hydrothermal method at 130 degrees C for 12 h. The samples characterized by XRD, SEM, TEM, SAED, and BET surface area. The nanosheet structure was slightly curved and approximately 50-100 nm in width and several nanometers in thickness. The as-synthesized nanosheet TiO2 had average pore diameter about 3-4 nm. The BET surface area and pore volume of the sample were about 642 m(2)/g and 0.774 cm(3)/g, respectively. The nanosheet structure after calcinations were changed into nanorods/nanoparticles composite with anatase TiO2 structure at 300-500 degrees C (10-15 nm in rods diameter and about 5-10 nm in particles diameter). The solar energy conversion efficiency (eta) of the cell using nanorods/nanoparticles TiO2 (from the nanosheet calcined at 450 degrees C for 2 h) with mesoporous structure was about 7.08% with Jsc of 16.35 mA/cm(2), Voc of 0.703 V and ff of 0.627; while eta of the cell using P-25 reached 5.82% with Jsc of 12.74 mA/cm(2), Voc of 0.704 V, and ff of 0.649.